LMM TOTAI offer a complete product and service portfolio for all steelmaking processes.
From basic and non-basic bricks and mixes, slide gate plates, isostatic products and prefab components to special machinery, mechanisms and repair systems.
Refractory for Cement Rotary Kiln
Brand: LMM YOTAI
Warranty: 1 year
Sample: Sample testing is available
Certification: ISO9001/ISO14001
Payment method: TT/LC
Shipping method: sea/land/air
Specifications: Customized products according to customer drawings
Refractory for Cement Rotary Kiln
The environments of transition zone, burning zone and cooling zone in cement rotary kiln are severe due to high temperature from burning clinker and erosion of K,Na,Cl,S.
The upsize of rotary kiln and usage in waste disposal make the condition of using refractories even harsher.
LMM Yotai group developed MgO-Cr203 series, MgO-Al203 Spinel series and non-chrome series bricks for cement rotary Kin, which have achieved remarkable results.
We occupy top shares in Japan refractory market, and have expanded greatly in China market as well.
Refractory for Sintering Zone of Rotary Kiln
Unit | MgO-Cr2O3. Brick | Dirdct-Bonded -MgO-Cr2O3. Brick | ||||||
LMM-MGE-10 | LMM-MGE-9 | LMM-MGE-8 | LMM-DMC-12 | LMM-DMC-110 | LMM-DMC-8 | |||
Apparent Porosity | % | 19.0 | 19.0 | 19.0 | 17.5 | 17.5 | 18.0 | |
Bulk Density | g/cm3 | 2.96 | 2.96 | 2.95 | 3.02 | 3.00 | 2.98 | |
Cold Crushing Strength | MPa | 40 | 40 | 40 | 45 | 45 | 45 | |
Refractoriness Under Load T2 | ℃ | 1580 | 1580 | 1580 | 1700 | 1700 | 1680 | |
Thermal Shock Resistance (1100℃-water) | Cycles | 5 | 5 | 5 | 6 | 6 | 6 | |
Chemical Composition | MgO | % | 70 | 70 | 72 | 70 | 75 | 77 |
Cr2O3. | 10 | 9 | 8 | 12 | 10 | 8 | ||
MgO-Cr2O3 Brick
A kind of silicate-combined basic firebrick fit for dry cement rotary kiln less than 2000t/d in capacity
Unit | Dirdct-Bonded MgO-Cr2O3. Brick | Hercynite Brick | MgO-Al2O3-ZrO2 Brick | |||||
LMM-RRR-U38 | LMM-RRR-U36T | LMM-RRR-U34 | LMM-YSP-SMT | LMM-PRA-NC-1 | LMM-PRA-NC-100NY | |||
Apparent Porosity | % | 17.5 | 18.0 | 18.0 | 17.0 | 17.0 | 16.0 | |
Bulk Density | g/cm3 | 3.03 | 3.00 | 3.00 | 2.93 | 2.92 | 2.93 | |
Cold Crushing Strength | MPa | 45 | 40 | 40 | 50 | 50 | 55 | |
Refractoriness Under Load T2 | ℃ | 1700 | 1700 | 1680 | 1700 | 1700 | 1700 | |
Thermal Shock Resistance (1100℃-water) | Cycles | 6 | 6 | 5 | 8 | 10 | 10 | |
Chemical Composition | MgO | % | 76 | 75 | 75 | 84 | 85 | 85 |
Al2O3 | 5 | 10 | 10 | |||||
Cr2O3. | 10 | 10 | 10 | |||||
Fe2O3 | 4 | |||||||
ZrO2 | 0.5 | 0.5 | ||||||
Dirdct-Bonded MgO-Cr2O3 Brick
A kind of basic bricks made from purer raw materials, shaped with high pressure and sintered under high temperature
Refractory brick production process
The manufacturing of refractory brick includes six general steps: mining and storage of raw materials, preparing raw materials, forming the brick, drying, firing and cooling, de-hacking, and storing finished products.
Quality Guarantee
The company ownis highly advanced automatic hydraulic press and tunnel kins capable of standing up ot 1850 celcius degrees. We manufacture various high-quality refractory products according to the clients’ needs, and to ensure the stability and account ability of the quality, we track and control the full manufaturing process through a variety of physical and chemical analysis.
Our company inherets the advanced technology, management experience and quality control from YOTAl. We have formed a comprehensive, effective and standarized management system with an excellent management team.
LMMYOTAI group devotes to the manufacture and research of refractory, design and construction of furnaces, while occupies top shares in cement rotary kiln, nonferrous metals, waste disposal and glass furnace in Japan.